Model#
[Main
ingredient] |
Curing
conditions
[irradiation
level &
time] |
Refraction
index (*1) |
Viscosity
(cP) |
Glass
transition
temperature
Tg (°C) |
Optical
transmittance%
[1.3um] |
Bond
Strength
(kgf/cm2) |
Special
Features |
Refractive
Index
Adjusting
Material
(High Tg)
[Epoxy](*2) |
30mW/cm2
10min |
1.46~1.57 |
200~560 |
130~137 |
89~90 |
120~>180 |
Modulate the refractive index to specific ＆#118alues for the best level of transparency. |
Refractive
Index
Adjusting
Material
(Low Tg)
[Epoxy] |
10mW/cm2
10min |
1.45~1.57 |
200~560 |
49~67 |
86~90 |
>180 |
Modulate the refractive index to specific ＆#118alues for the best level of transparency. |
GA700H
(High Tg)
[Epoxy](*2) |
30mW/cm2
10min |
1.46 |
252 |
138 |
93 |
94 |
At λ1.55um, adjusted to match silica glass |
GA700L
(Low Tg)
[Epoxy] |
10mW/cm2
5min |
1.46 |
250 |
49 |
94 |
>200 |
At λ1.55um, adjusted to match silica glass |
AT6001
[Acrylate] |
10mW/cm2
10min |
1.51 |
440 |
-3 |
91 |
>150 |
Telecordia standard (strong under high temperature and humidity, flexible) |
AT8224
[Acrylate] |
10mW/cm2
5min |
1.51 |
180 |
111 |
89 |
>122 |
Telecordia standard (strong under high temperature and humidity, High Tg) |
AT6390
[Acrylate] |
10mW/cm2
5min |
1.51 |
840 |
100 |
90 |
156 |
High endurance material,
Tg > 100°C,
High viscosity |